热活化煤矸石-水泥复合体系水化性能分析.pdf
文档页数：4文档大小：428.1KB文档格式：pdf粉煤灰综合利用 2012No.2 FLY ASH COMPREHENSIVE UTILIZATION研究 热活化煤石-水泥复合体系水化性能分析 Research on Hydration Properties of Blended Cement based on Thermal Activated Coal Gangue何燕 (同济大学材料科学与工程学院建筑材料研究所,上海201804) 要:采用比强度法对活化煤研石的火山灰效应进行评定,通过Ca(OH)2剩余量和化学结合水量的测定,分析活 化煤矸石水泥体系的水化程度,并采用X射线衍射分析,差热分析对其水化过程进行研究。结果表明:煅烧温度为 750℃,保温时间为4h的热活化煤矸石对水泥体系的火山灰贡献率较高;该体系Ca(OH)2剩余量较少,化学结合水量较 多,其水化产物主要以Cs凝胶,Ca(OH)2和钙矾石为主。 关键词:煤矸石热活化水化性能 中图分类号:TQ172.78*2 献标识码:文章编号:1005-8249(2012)02-0014 He YanCollege Material Science and Technology ,Tongji University ,Shanghai 201804 ) Abstract :By specifie strength concept ,the pozzolanic effect of activated coal gangue could be investigated .Through the content of Ca( )2surplus and the amount of chemically bined water ,the hydration degree of activated coal gangue-cement system could be investigatod . By means of X-ray diffraction and Differential Thermal Analysis etc ,the hydration process of the cement system with activated coal gangue could化反应的早期其填充作用较明显,使集料与浆体的界 (3)磨细粉煤灰中<20m的颗粒粒径对其活性 面缺陷减少,致密性提高,大幅度提高了强度,进一步 影响较大,粉磨时间对抗折强度活性指数的影响比抗 延长粉磨时间则效果不显著;后期粉煤灰火山灰活性 压强度活性指数的影响较大,粉磨10min对7d抗压强 起主要作用,粉煤灰细度的减小,增加了粉煤灰颗粒的 度活性指数的影响较显著。 反应面积,使浆体中的水化产物增多,后期强度有一定 参考文献 程度的增加。 [1]文梓芸,钱春香等混...
本文来自呆头呆脑的猪投稿，不代表文丁图集立场，如若转载，请注明出处：https://www.2b34.com/blog/103083.html
微信扫一扫 